Now that is a nice piece of work. It pretty much demonstrates most of what I have been saying for a long time. Kills my perception that exfoliation of the basic Fullerene shape is the primary lubricating mechanism; got to change my mental store to ball bearings. Although they did mention chunks filling holes after being sheered off the Fullerenes.
ChiaroBlue, that link should be posted in the MS2 thread subject matter. If you don't want to do it, send a PM and I will. Thanks for posting it.
Did anyone here attend that meeting? If you have, some feedback from the audience would be nice.